The influence of hydrothermal fatigue on the clinically relevant functional properties of conventional glass-ionomer cements.

During their everyday service, the restorative dental materials are subjected to temperature changes which can be viewed as intensive in the context of the highest allowed temperatures for these materials. In this work, the effect of hydrothermal fatigue on the in vitro tribological performance, compression strength, microhardness, and surface roughness of glass-ionomer cements was studied. Samples of 3 commercially available cements were divided into the reference (aged 14 days) and thermocycled (20,000 cycles; 5-55 °C) groups. The results obtained show that functional properties of the specimens subjected to thermal fatigue significantly differ from the literature data on the cements aged at constant temperatures. The effect of hydrothermal fatigue on the functional properties of cements is discussed in the context of processes induced by exposure to variable temperatures.

Effect of Hydrothermal Factors on the Microhardness of Bulk-Fill and Nanohybrid Composites.

This study evaluates the effect of aging in artificial saliva and thermal shocks on the microhardness of the bulk-fill composite compared to the nanohybrid composite. Two commercial composites, Filtek Z550 (3M ESPE) (Z550) and Filtek Bulk-Fill (3M ESPE) (B-F), were tested. The samples were exposed to artificial saliva (AS) for one month (control group). Then, 50% of the samples from each composite were subjected to thermal cycling (temperature range: 5-55 °C, cycle time: 30 s, number of cycles: 10,000) and another 50% were put back into the laboratory incubator for another 25 months of aging in artificial saliva. The samples' microhardness was measured using the Knoop method after each stage of conditioning (after 1 month, after 10,000 thermocycles, after another 25 months of aging). The two composites in the control group differed considerably in hardness (HK = 89 for Z550, HK = 61 for B-F). After thermocycling, the microhardness decrease was for Z550 approximately 22-24% and for B-F approximately 12-15%. Hardness after 26 months of aging decreased for Z550 (approximately 3-5%) and B-F (15-17%). B-F had a significantly lower initial hardness than Z550, but it showed an approximately 10% lower relative reduction in hardness.